Semiconductor substrate structure

ABSTRACT

A process for producing monocrystalline semiconductor layers. In an exemplary embodiment, a graded Si 1-x Ge x  (x increases from 0 to y) is deposited on a first silicon substrate, followed by deposition of a relaxed Si 1-y Ge y  layer, a thin strained Si 1-z Ge z  layer and another relaxed Si 1-y Ge y  layer. Hydrogen ions are then introduced into the strained Si z Ge z  layer. The relaxed Si 1-y Ge y  layer is bonded to a second oxidized substrate. An annealing treatment splits the bonded pair at the strained Si layer, such that the second relaxed Si 1-y Ge y  layer remains on the second substrate. In another exemplary embodiment, a graded Si 1-x Ge x  is deposited on a first silicon substrate, where the Ge concentration x is increased from 0 to 1. Then a relaxed GaAs layer is deposited on the relaxed Ge buffer. As the lattice constant of GaAs is close to that of Ge, GaAs has high quality with limited dislocation defects. Hydrogen ions are introduced into the relaxed GaAs layer at the selected depth. The relaxed GaAs layer is bonded to a second oxidized substrate. An annealing treatment splits the bonded pair at the hydrogen ion rich layer, such that the upper portion of relaxed GaAs layer remains on the second substrate.

PRIORITY INFORMATION

[0001] This application claims priority from provisional application Ser. No. 60/225,666 filed Aug. 16, 2000.

BACKGROUND OF THE INVENTION

[0002] The present invention relates to a production of a general substrate of relaxed Si_(1-x)Ge_(x)-on-insulator (SGOI) for various electronics or optoelectronics applications, and the production of monocrystalline III-V or II-VI material-on-insulator substrate.

[0003] Relaxed Si_(1-x)Ge_(x)-on-insulator (SGOI) is a very promising technology as it combines the benefits of two advanced technologies: the conventional SOI technology and the disruptive SiGe technology. The SOI configuration offers various advantages associated with the insulating substrate, namely reduced parasitic capacitances, improved isolation, reduced short-channel-effect, etc. High mobility strained-Si, strained-Si_(1-x)Ge_(x) or strained-Ge MOS devices can be made on SGOI substrates.

[0004] Other III-V optoelectronic devices can also be integrated into the SGOI substrate by matching the lattice constants of III-V materials and the relaxed Si_(1-x)Ge_(x). For example a GaAs layer can be grown on Si_(1-x)Ge_(x)-on-insulator where x is equal or close to 1. SGOI may serve as an ultimate platform for high speed, low power electronic and optoelectronic applications.

[0005] SGOI has been fabricated by several methods in the prior art. In one method, the separation by implantation of oxygen (SIMOX) technology is used to produce SGOI. High dose oxygen implant was used to bury high concentrations of oxygen in a Si_(1-x)Ge_(x) layer, which was then converted into a buried oxide (BOX) layer upon annealing at high temperature (for example, 1350° C.). See, for example, Mizuno et al. IEEE Electron Device Letters, Vol. 21, No. 5, pp. 230-232, 2000 and Ishilawa et al. Applied Physics Letters, Vol. 75, No. 7, pp. 983-985, 1999. One of the main drawbacks is the quality of the resulting Si_(1-x)Ge_(x) film and BOX. In addition, Ge segregation during high temperature anneal also limits the maximum Ge composition to a low value.

[0006] U.S. Pat. Nos. 5,461,243 and 5,759,898 describe a second method, in which a conventional silicon-on-insulator (SOI) substrate was used as a compliant substrate. In the process, an initially strained Si_(1-x)Ge_(x) layer was deposited on a thin SOI substrate. Upon an anneal treatment, the strain was transferred to the thin silicon film underneath, resulting in relaxation of the top Si_(1-x)Ge_(x) film. The final structure is relaxed-SiGe/strained-Si/insulator, which is not an ideal SGOI structure. The silicon layer in the structure is unnecessary, and may complicate or undermine the performance of devices built on it. For example, it may form a parasitic back channel on this strained-Si, or may confine unwanted electrons due to the band gap offset between the strained-Si and SiGe layer.

[0007] U.S. Pat. Nos. 5,906,951 and 6,059,895 describe the formation of a similar SGOI structure: strained-layer(s)/relaxed-SiGe/Si/insulator structure. The structure was produced by wafer bonding and etch back process using a P⁺⁺ layer as an etch stop. The presence of the silicon layer in the above structure may be for the purpose of facilitating Si-insulator wafer bonding, but is unnecessary for ideal SGOI substrates. Again, the silicon layer may also complicate or undermine the performance of devices built on it. For example, it may form a parasitic back channel on this strained-Si, or may confine unwanted electrons due to the band gap offset between the strained-Si and SiGe layer. Moreover, the etch stop of P⁺⁺ in the above structure is not practical when the first graded Si_(1-y)Ge_(y) layer described in the patents has a y value of larger than 0.2. Experiments from research shows Si_(1-y)Ge_(y) with y larger than 0.2 is a very good etch stop for both KOH and TMAH, as described in a published PCT application WO 99/53539. Therefore, the KOH will not be able to remove the first graded Si_(1-y)Ge_(y) layer and the second relaxed SiGe layer as described in the patents.

[0008] Other attempts include re-crystallization of an amorphous Si_(1-x)Ge_(x) layer deposited on the top of SOI (silicon-on-insulator) substrate, which is again not an ideal SGOI substrate and the silicon layer is unnecessary, and may complicate or undermine the performance of devices built on it. Note Yeo et al. IEEE Electron Device Letters, Vol. 21, No. 4, pp. 161-163, 2000. The relaxation of the resultant SiGe film and quality of the resulting structure are main concerns.

[0009] From the above, there is a need for a simple technique for relaxed SGOI substrate production, a need for a technique for production of high quality SGOI and other III-V material-on-insulator, and a need for a technique for wide range of material transfer.

SUMMARY OF THE INVENTION

[0010] According to the invention, there is provided an improved technique for production of wide range of high quality material is provided. In particular, the production of relaxed Si_(1-x)Ge_(x)-on-insulator (SGOI) substrate or relaxed III-V or II-VI material-on-insulator, such as GaAs-on-insulator, is described. High quality monocrystalline relaxed SiGe layer, relaxed Ge layer, or other relaxed III-V material layer is grown on a silicon substrate using a graded Si_(1-x)Ge_(x) epitaxial growth technique. A thin film of the layer is transferred into an oxidized handle wafer by wafer bonding and wafer splitting using hydrogen ion implantation. The invention makes use of the graded Si_(1-x)Ge_(x) buffer structure, resulting in a simplified and improved process.

[0011] The invention also provides a method allowing a wide range of device materials to be integrated into the inexpensive silicon substrate. For example, it allows production of Si_(1-x)Ge_(x)-on-insulator with wide range of Ge concentration, and allows production of many III-V or II-VI materials on insulator like GaAs, AlAs, ZnSe and InGaP. The use of graded Si_(1-x)Ge_(x) buffer in the invention allows high quality materials with limited dislocation defects to be produced and transferred. In one example, SGOI is produced using a SiGe structure in which a region in the graded buffer can act as a natural etch stop.

[0012] The invention provides a process and method for producing monocrystalline semiconductor layers. In an exemplary embodiment, a graded Si_(1-x)Ge_(x) (x increases from 0 to y) is deposited on a first silicon substrate, followed by deposition of a relaxed Si_(1-y) Ge_(y) layer, a thin strained Si_(1-z)Ge_(z) layer and another relaxed Si_(1-y)Ge_(y) layer. Hydrogen ions are then introduced into the strained Si_(1-z)Ge_(z) layer. The relaxed Si_(1-y)Ge_(y) layer is bonded to a second oxidized substrate. An annealing treatment splits the bonded pair at the strained Si layer, whereby the second relaxed Si_(1-y)Ge_(y) layer remains on said second substrate.

[0013] In another exemplary embodiment, a graded Si_(1-x)Ge_(x) is deposited on a first silicon substrate, where the Ge concentration x is increased from 0 to 1. Then a relaxed GaAs layer is deposited on the relaxed Ge buffer. As the lattice constant of GaAs is close to that of Ge, GaAs has high quality with limited dislocation defects. Hydrogen ions are introduced into the relaxed GaAs layer at the selected depth. The relaxed GaAs layer is bonded to a second oxidized substrate. An annealing treatment splits the bonded pair at the hydrogen ion rich layer, whereby the upper portion of relaxed GaAs layer remains on said second substrate.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014]FIGS. 1A-1C are block diagrams showing the process of producing a SGOI substrate in accordance with the invention;

[0015]FIGS. 2A and 2B are infrared transmission images of an as-bonded wafer pair and a final SGOI substrate after splitting, respectively;

[0016]FIG. 3 is a TEM cross-section view of a SiGe layer that was transferred onto the top of a buried oxide;

[0017]FIG. 4 is an AFM for a transferred SGOI substrate showing surface roughness; and

[0018]FIGS. 5-8 are block diagrams of various exemplary embodiments semiconductor structures in accordance with the invention.

DETAILED DESCRIPTION OF THE INVENTION

[0019] An example of a process in which SGOI is created by layer transfer is described. The experiment was performed in two stages. In the first stage, heteroepitaxial SiGe layers are formed by a graded epitaxial growth technology. Starting with a 4-inch Si (100) donor wafer 100, a linearly stepwise compositionally graded Si_(1-x)Ge_(x) buffer 102 is deposited with CVD, by increasing Ge concentration from zero to 25%. Then a 2.5 μm relaxed Si_(0.75)Ge_(0.25) cap layer 104 is deposited with the final Ge composition, as shown in FIG. 1A.

[0020] The relaxed SiGe cap layer has high quality with very low dislocation defect density (less than 1E6/cm²), as the graded buffer accommodates the lattice mismatch between Si and relaxed SiGe. A thin layer of this high quality SiGe will be transferred into the final SGOI structure. The surface of the as-grown relaxed SiGe layer shows a high roughness around 11 nm to 15 nm due to the underlying strain fields generated by misfit dislocations at the graded layer interfaces and thus chemical-mechanical polishing (CMP) is used to smooth the surface. In the second stage, the donor wafer is implanted with hydrogen ion (100 keV, 5E16 H⁺/cm²) to form a buried hydrogen-rich layer. After a surface clean step in a modified RCA solution, it is bonded to an oxidized 106 Si handle wafer 108 at room temperature as shown in FIG. 1B.

[0021] The wafer bonding is one of the key steps, and the bonding energy should be strong enough in order to sustain the subsequent layer transfer in the next step. Good bonding requires a flat surface and a highly hydrophilic surface before bonding. On the other hand, the buried oxide in the final bonded structure is also required to have good electrical properties as it will influence the final device fabricated on it. In the conventional Si film transfer, thermal oxide on the donor wafer is commonly used before H⁺ implantation and wafer bonding, which becomes the buried oxide in the resulting silicon-on-insulator structure.

[0022] The thermal oxide of the Si donor wafer meets all the requirements, as it has good electrical properties, has flat surface and bonds very well to the handle wafer. Unlike the Si, however, the oxidation of SiGe film results in poor thermal oxide quality, and the Ge segregation during oxidation also degrades the SiGe film. Therefore the thermal oxide of SiGe is not suitable for the SGOI fabrication. In one exemplary experiment the SiGe film will be directly bonded to an oxidized Si handle wafer. The high quality thermal oxide in the handle wafer will become the buried oxide in the final SGOI structure.

[0023] Having a flat surface after a CMP step, the SiGe wafer went through a clean step. Compared to Si, one difficulty of SiGe film is that, SiGe surface becomes rougher during the standard RCA clean, as the NH₄OH in RCA1 solution etches Ge faster than Si. Rough surface will lead to weak bonding as the contact area is reduced when bonded to the handle wafer. In this exemplary embodiment, H₂SO₄—H₂O₂ solution is used in the place of RCA1, which also meets the clean process requirement for the subsequent furnace annealing after bonding. The SiGe surface after H₂SO₄—H₂O₂ clean shows better surface roughness compared to RCA1.

[0024] After this modified clean procedure, the SiGe wafer is dipped in the diluted HF solution to remove the old native oxide. It is then rinsed in DI water thoroughly to make the surface hydrophilic by forming a fresh new native oxide layer that is highly active. After spinning dry, the SiGe wafer is bonded to an oxidized handle wafer at room temperature, and then annealed at 600° C. for 3 hours. During anneal the bonded pair split into two sheets along the buried hydrogen-rich layer, and a thin relaxed Si_(0.75)Ge_(0.25) film 110 is transferred into the handle wafer, resulting in a SGOI substrate 112, as shown in FIG. 1B. A final 850° C. anneal improves the Si_(0.75)Ge_(0.25)/SiO₂ bond. Thereafter, device layers 114 can be processed on the SGOI substrate 112 as shown in FIG. 1C.

[0025]FIGS. 2A and 2B are infrared transmission images of the as-bonded wafer pair and the final SGOI substrate after splitting, respectively. To investigate the surface of the as-transferred SGOI substrate, transmission electron microscopy (TEM) and atomic force microscopy (AFM) were used. The TEM cross-section view in FIG. 3 shows a ˜640 nm SiGe layer was transferred onto the top of a 550 nm buried oxide (BOX). Surface damage is also shown clearly at the splitting surface with a damage depth of ˜100 nm.

[0026]FIG. 4 shows a surface roughness of 11.3 nm in an area of 5×5 μm² by AFM for the as-transferred SGOI. The data is similar to those from as-transferred silicon film by smart-cut process, and suggests that a top layer of about 100 nm should be removed by a final CMP step. After SiGe film transferring, only a thin relaxed SiGe film is removed and the donor wafer can be used again for a donor wafer. Starting from this general SGOI substrate, various device structures can be realized by growing one or more device layers on the top, as shown in FIG. 2C. Electrical evaluation is in progress by growing a strain Si layer on the top of this SGOI substrate followed by fabrication of strained Si channel devices.

[0027] Bond strength is important to the process of the invention. AFM measurements were conducted to investigate the SiGe film surface roughness before bonding under different conditions. One experiment is designed to investigate how long the SiGe surface should be polished to have smooth surface and good bond strength, since the surface of the as-grown relaxed SiGe layer has a high roughness around 11 nm to 15 nm. Several identical 4-inch Si wafers with relaxed Si_(0.75)Ge_(0.25) films were CMPed with optimized polishing conditions for different times. Using AFM, the measured surface mircoroughness RMS at an area of 10 μm×10 μm is 5.5 Å, 4.5Å and 3.8 Å, for wafer CMPed for 2 min., 4 min. and 6 min. respectively. After bonding to identical handle wafers, the tested bond strength increases with decreasing RMS. A CMP time of 6 min. is necessary for good strength.

[0028] In another experiment, two identical 4-inch Si wafers with relaxed Si_(0.75)Ge_(0.25) films were CMPed for 8 min. After two cleaning steps in H₂SO₄:H₂O₂ solution and one step in diluted HF solution, one wafer was put in a new H₂SO₄:H₂O₂ (3:1) solution and another in a new NH₄OH:H₂O₂:H₂O (1:1:5), i.e. the conventional RCA1 solution, both for 15 min. The resultant wafers were tested using AFM. The wafer after H₂S0 ₄:H₂O₂ solution shows a surface roughness RMS of 2 Å at an area of 1 μm×1 μm, which after NH₄OH:H₂O₂:H₂O shows 4.4 Å. Clearly, the conventional RCA clean roughens the SiGe surface significantly, and H₂SO₄:H₂O₂ should be used for SiGe clean.

[0029] In yet another experiment, the clean procedure is optimized before bonding. For direct SiGe wafer to oxidized handle wafer bonding (SiGe-oxide bonding), several different clean procedures were tested. It has been found that the H₂SO₄:H₂O₂ (2˜4:1) solution followed by DI water rinse and spin dry gives good bond strength. Alternatively, one can also deposit an oxide layer on the SiGe wafer and then CMP the oxide layer. In this case SiGe/oxide is bonded to an oxidized handle wafer, i.e. oxide-oxide bonding. Among different clean procedures, it was found that NH₄OH:H₂O₂:H₂O clean and DI water rinse following by diluted HF, DI water rinse and spin dry gives very good bond strength.

[0030]FIG. 5 is a block diagram of an exemplary embodiment of a semiconductor structure 500 in accordance with the invention. A graded Si_(1-x)Ge_(x) buffer layer 504 is grown on a silicon substrate 502, where the Ge concentration x is increased from zero to a value y in a stepwise manner, and y has a selected value between 0 and 1. A second relaxed Si_(1-y)Ge_(y) layer 506 is then deposited, and hydrogen ions are implanted into this layer with a selected depth by adjusting implantation energy, forming a buried hydrogen-rich layer 508. The wafer is cleaned and bonded to an oxidized handle wafer 510. An anneal treatment at 500˜600° C. splits the bonded pair at the hydrogen-rich layer 508. As a result, the upper portion of the relaxed Si_(1-y)Ge_(y) layer 506 remains on the oxidized handle wafer, forming a SGOI substrate. The above description also includes production of Ge-on-insulator where y=1.

[0031] During the wafer clean step prior to bonding, the standard RCA clean for the silicon surface is modified. Since the NH₄OH in standard RCA1 solution etches Ge faster than Si, the SiGe surface will become rough, leading to a weak bond. A H₂SO₄—H₂O₂ solution is used in the place of RCA1, which also meets the clean process requirement for the subsequent furnace annealing after bonding. The SiGe surface after the H₂SO₄—H₂O₂ clean showed better surface roughness compared to RCA1. After the modified RCA clean, the wafers are then immersed in another fresh H₂SO₄—H₂O₂ solution for 10 to 20 min. H₂SO₄—H₂O₂ renders the SiGe surface hydrophilic. After a rinse in DI wafer and spin drying, the SiGe wafer is bonded to an oxidized handle wafer at room temperature immediately, and then annealed at 500˜600° C. for wafer splitting.

[0032]FIG. 6 is a block diagram of another exemplary embodiment of a semiconductor structure 600. The structure 600 includes a graded Si_(1-x)Ge_(x) buffer layer 604 grown on a silicon substrate 602, where the Ge concentration x is increased from zero to 1. Then a relaxed pure Ge layer 606 and a III-V material layer 608, such as a GaAs layer, are epitaxially grown on the Ge layer. Hydrogen ions are implanted into the GaAs layer 608 with a selected depth by adjusting implantation energy, forming a buried hydrogen-rich layer 610. The wafer is cleaned and bonded to an oxidized handle wafer 612. An anneal treatment splits the bonded pair at the hydrogen-rich layer 610. As a result, the upper portion of the GaAs layer 608 remains on the oxidized handle wafer, forming a GaAs-on-insulator substrate.

[0033]FIG. 7 is a block diagram of yet another exemplary embodiment of a semiconductor structure 700. A graded Si_(1-x)Ge_(x) buffer layer 704 is grown on a silicon substrate 702, where the Ge concentration x is increased from zero to a selected value y, where is less than 0.2. A second relaxed Si_(1-z)Ge_(x) layer 706 is deposited, where z is between 0.2 to 0.25. Hydrogen ions are implanted into the graded Si_(1-x)Ge_(x) buffer layer 704 with a selected depth, forming a buried hydrogen-rich layer 708 within layer 704. The wafer is cleaned and bonded to an oxidized handle wafer 710. An anneal treatment at 500˜600° C. splits the bonded pair at the hydrogen-rich layer 708.

[0034] As a result, the upper portion of the graded Si_(1-x)Ge_(x) buffer layer 704 and the relaxed Si_(1-z)Ge_(z) layer 706 remains on the oxidized handle wafer 710. The remaining graded Si_(1-x)Ge_(x) buffer layer 704 is then selectively etched by either KOH or TMAH. KOH and TMAH etch Si_(1-x)Ge_(x) fast when x is less 0.2, but becomes very slow when x is larger than 0.2. Thus, the graded Si_(1-x)Ge_(x) buffer layer 704 can be etched selectively, leaving the relaxed Si_(1-z)Ge_(z) layer 706 on the insulating substrate 710 and forming a relaxed SGOI substrate. In this process, the thickness of the relaxed Si_(1-z)Ge_(z) film 706 on the final SGOI structure is defined by film growth, which is desired in some applications.

[0035]FIG. 8 is a block diagram of yet another exemplary embodiment of a semiconductor structure 800. A graded Si_(1-x)Ge_(x) buffer layer 804 is grown on a silicon substrate 802, where the Ge concentration x is increased from zero to a selected value y between 0 and 1. A second relaxed Si_(1-y)Ge_(y) layer 806 is deposited, followed by a strained Si_(1-z)Ge_(z) layer 808 and another relaxed Si_(1-z)Ge_(y) layer 810. The thickness of layers 806, 808, and 810, and the value z are chosen such that the Si_(1-z)Ge_(z) layer 808 is under equilibrium strain state while the Si_(1-y)Ge_(y) layers 806 and 810 remain relaxed. In one option, hydrogen ions may be introduced into the strained Si_(1-z)Ge_(z) layer 808, forming a hydrogen-rich layer 812. The wafer is cleaned and bonded to an oxidized handle wafer 814. The bonded pair is then separated along the strained Si_(1-z)Ge_(z) layer 808.

[0036] Since the strain makes the layer weaker, the crack propagates along this layer during separation. The separation can be accomplished by a variety of techniques, for example using a mechanical force or an anneal treatment at 500˜600° C. when the hydrogen is also introduced. See, for example, U.S. Pat. Nos. 6,033,974 and 6,184,111, both of which are incorporated herein by reference. As a result, the relaxed Si_(1-y)Ge_(y) layer 810 remains on the oxidized handle wafer, forming a relaxed SGOI substrate. The thickness of layers 806, 808, and 810, and the value z may also be chosen such that there are a good amount of dislocations present in the Si_(1-z)Ge_(z) layer 808 while the top Si_(1-y)Ge_(y) layer 810 remains relaxed and having high quality and limited dislocation defects.

[0037] These dislocation defects in the Si_(1-z)Ge_(z) layer 808 can then act as hydrogen trap centers during the subsequent step of introducing ions. The hydrogen ions may be introduced by various ways, such as ion implantation or ion diffusion or drift by means of electrolytic charging. The value of z may be chosen in such a way that the remaining Si_(1-z)Ge_(z) layer 808 can be etched selectively by KOH or TMAH. The layers 806 and 810 may also be some other materials, for example pure Ge, or some III-V materials, under the condition that the Ge concentration x in the graded Si_(1-x)Ge_(x) buffer layer 804 is increased from zero to 1.

[0038] After all the semiconductor-on-insulator substrate obtained by the approaches described above, various device layers can be further grown on the top. Before the regrowth, CMP maybe used to polish the surface.

[0039] Although the present invention has been shown and described with respect to several preferred embodiments thereof, various changes, omissions and additions to the form and detail thereof, may be made therein, without departing from the spirit and scope of the invention. 

What is claimed is:
 1. A process of forming a semiconductor structure with a relaxed Si_(1-y)Ge_(y) layer, comprising: depositing a graded Si_(1-x)Ge_(x) buffer layer on a first substrate, wherein said Ge concentration x is increased from zero to a value y; depositing a relaxed Si_(1-y)Ge_(y) layer; introducing ions into said relaxed Si_(1-y)Ge_(y) layer to define a first heterostructure; bonding said first heterostructure to a second substrate to define a second heterostructure; splitting said second heterostructure in the region of the introduced ions, wherein a top portion of said relaxed Si_(1-y)Ge_(y) layer remains on said second substrate.
 2. The process of claim 1 further comprising forming at least one device layer or a plurality of integrated circuit devices, after said step of depositing said relaxed Si_(1-y)Ge_(y) layer.
 3. The process of claim 2, wherein said at least one device layer comprises at least one of strained Si, strained Si_(1-w)Ge_(w) with w≠y, strained Ge, GaAs, AlAs, ZnSe and InGaP.
 4. The process of claim 1 further comprising forming an insulating layer before said step of introducing ions.
 5. The process of claim 1 further comprising planarizing said relaxed Si_(1-y)Ge_(y) layer, before said step of introducing ions.
 6. The process of claim 1, wherein said ions comprise hydrogen H⁺ ions or H₂ ⁺ ions.
 7. The process of claim 1 further comprising planarizing said relaxed Si_(1-y)Ge_(y) layer, after said step of introducing ions.
 8. The process of claim 1 further comprising cleaning both said first heterostructure and said second substrate, before said step of bonding.
 9. The process of claim 1, wherein said second heterostructure is split by annealing.
 10. The process of claim 1, wherein said second heterostructure is split by annealing followed by mechanical force.
 11. The process of claim 1 further comprising removing the top portion of the remaining of said relaxed Si_(1-y)Ge_(y) layer, after said step of splitting.
 12. The process of claim 1 further comprising forming at least one device layer, or a plurality of integrated circuit devices, after said step of splitting.
 13. The process of claim 12, wherein said at least one device layer comprises at least one of relaxed Si_(1-y)Ge_(y), strained Si, strained Si_(1-w)Ge_(w), strained Ge, GaAs, AlAs, ZnSe and InGaP.
 14. The process of claim 1 further comprising re-using the remaining first heterostructure, after said step of splitting.
 15. The process of claim 1, wherein said first substrate comprises monocrystalline silicon.
 16. A process of forming a semiconductor layer, comprising: depositing a graded Si_(1-x)Ge_(x) buffer layer on a first substrate, said Ge concentration x being increased from zero to 1; depositing a relaxed Ge layer; forming a monocrystalline semiconductor layer including another material whose lattice constant is approximately close to that of Ge; introducing ions into said semiconductor layer to define a first heterostructure; bonding said first heterostructure to a second substrate to define a second heterostructure; splitting said second heterostructure in the region of introduced ions, wherein a top portion of said semiconductor layer remains on said second substrate.
 17. The process of claim 16, wherein said semiconductor layer comprises one of GaAs, AlAs, ZnSe and InGaP.
 18. The process of claim 16 further comprising forming at least one device layer or a plurality of integrated circuit devices, after said step of forming said semiconductor layer.
 19. The process of claim 16 further comprising forming an insulating layer before said step of introducing ions.
 20. The process of claim 16 further comprising planarizing said semiconductor layer before said step of introducing ions.
 21. The process of claim 16, wherein said ions comprise hydrogen H⁺ ions or H₂ ⁺ ions.
 22. The process of claim 16, further comprising the step of planarizing said semiconductor layer after said step of introducing ions.
 23. The process of claim 16 further comprising cleaning both said first heterostructure and said second substrate, before said step of bonding.
 24. The process of claim 16, wherein said second heterostructure is split by annealing.
 25. The process of claim 16, wherein said second heterostructure is split by annealing and followed by mechanical force.
 26. The process of claim 16 further comprising removing the top portion of the remaining of said third semiconductor layer, after said step of splitting.
 27. The process of claim 16 further comprising forming at least one device layer or a plurality of integrated circuit devices, after said step of splitting.
 28. The process of claim 16 further comprising re-using the remaining first heterostructure, after said step of splitting.
 29. The process of claim 16, wherein said first substrate comprises monocrystalline silicon.
 30. A process of forming a semiconductor structure with a relaxed Si_(1-z)Ge_(z) layer, comprising: depositing a graded Si_(1-x)Ge_(x) buffer layer on a first substrate, said Ge concentration x being increased from zero to a selected value y, and y being less than 0.2; depositing a relaxed Si_(1-z)Ge_(z) layer, where z is between 0.2 and 0.25; introducing ions into said graded Si_(1-x)Ge_(x) buffer layer to define a first heterostructure; bonding said first heterostructure to a second substrate to define a second heterostructure; splitting said second heterostructure in the region of introduced ions, wherein the upper portion of first graded Si_(1-x)Ge_(x) layer and said relaxed Si_(1-z)Ge_(z) layer remains on said second substrate; and selectively etching the remaining portion of said graded Si_(1-x)Ge_(x) layer, wherein said relaxed Si_(1-z)Ge_(z) layer remains on said second substrate.
 31. The process of claim 30 further comprising forming at least one device layer or a plurality of integrated circuit devices, after said step of forming said relaxed Si_(1-z)Ge_(z) layer.
 32. The process of claim 31, wherein said at least one device layer includes one or more of strained Si, strained Si_(1-w)Ge_(w) with w≠z, and strained Ge.
 33. The process of claim 30 further comprising forming an insulating layer before said step of introducing ions.
 34. The process of claim 30 further comprising planarizing said relaxed Si_(1-z)Ge_(z) layer before said step of introducing ions.
 35. The process of claim 30, wherein said ions comprise hydrogen H⁺ ions or H₂ ⁺ ions.
 36. The process of claim 30 further comprising planarizing the relaxed Si_(1-z)Ge_(z) layer after said step of introducing ions.
 37. The process of claim 30 further comprising cleaning both said first heterostructure and said second substrate, before said step of bonding.
 38. The process of claim 30, wherein said second heterostructure is split by annealing.
 39. The process of claim 30 further comprising planarizing said second relaxed Si_(1-z)Ge_(z) layer after said step of etching.
 40. The process of claim 30 further comprising forming at least one device layer or a plurality of integrated circuit devices, after said step of etching.
 41. A process of forming a semiconductor layer, comprising: depositing a graded Si_(1-x)Ge_(x) buffer layer on a first substrate, said Ge concentration x being increased from zero to a value y; depositing a relaxed Si_(1-y)Ge_(y) layer; depositing a strained or defect layer; depositing a relaxed layer; introducing ions into said strained or defect layer to define a first heterostructure; bonding said first heterostructure to a second substrate to define a second heterostructure; and splitting said second heterostructure in the region of the strained or defect layer, wherein said relaxed layer remains on said second substrate.
 42. The process of claim 41, wherein said strained or defect layer comprises either a strained Si_(1-z)Ge_(z) layer with z≠y, or other III-V material.
 43. The process of claim 41, wherein said relaxed layer or said strained or defect layer comprises either a relaxed Si_(1-w)Ge_(w) layer where w is close or equal to y, or, when y is equal to 1, one of Ge, GaAs, AlAs, ZnSe and InGaP.
 44. The process of claim 41 further comprising forming at least one device layer or a plurality of integrated circuit devices, after said step of depositing said relaxed layer.
 45. The process of claim 41 further comprising forming an insulating layer before said step of introducing ions.
 46. The process of claim 41 further comprising planarizing said relaxed layer before said step of introducing ions.
 47. The process of claim 41, wherein said ions comprise hydrogen H⁺ ions or H₂ ⁺ ions.
 48. The process of claim 41 further comprising planarizing said relaxed layer after said step of introducing ions.
 49. The process of claim 41 further comprising cleaning both said first heterostructure and said second substrate, before said step of bonding.
 50. The process of claim 41, wherein said second heterostructure is split by annealing.
 51. The process of claim 41 further comprising removing one of any remaining of said strained or defect layer, and the top portion of said relaxed layer, after said step of splitting.
 52. The process of claim 41 further comprising forming at least one device layer or a plurality of integrated circuit devices, after said step of splitting.
 53. The process of claim 41 further comprising re-using the remaining first heterostructure for a subsequent process after planarizing.
 54. A semiconductor structure comprising: a first semiconductor substrate; a second layer of relaxed Si_(1-x)Ge_(x), wherein x=0.1 to 1; and a third layer comprising at least one of GaAs, AlAs, ZnSe and InGaP, or strained Si_(1-y)Ge_(y) wherein y≠x.
 55. A semiconductor structure comprising: a first substrate comprising monocrystalline silicon substrate; a second layer of graded Si_(1-x)Ge_(x) buffer layer, wherein said Ge concentration x is increased from zero to a value y; a third layer of relaxed Si_(1-y)Ge_(y); a fourth strained or defect layer comprising either a strained Si_(1-z)Ge_(z) layer with z≠y, or other III-V or II-VI material; and a fifth relaxed layer comprising either a relaxed Si_(1-w)Ge_(w) layer where w is close or equal to y, or, when y is equal to 1, at least one of Ge, GaAs, AlAs, ZnSe and InGaP. 